Microstructural deformation process of shock-compressed polycrystalline aluminum

Scientific Reports volume 9, Article number: 7604 (2019) Cite this article

4261 Accesses

29 Citations

29 Altmetric

Metrics details

Plastic deformation of polycrystalline materials under shock wave loading is a critical characteristic in material science and engineering. However, owing to the nanosecond time scale of the shock-induced deformation process, we currently have a poor mechanistic understanding of the structural changes from atomic scale to mesoscale. Here, we observed the dynamic grain refinement of polycrystalline aluminum foil under laser-driven shock wave loading using time-resolved X-ray diffraction. Diffraction spots on the Debye-Scherrer ring from micrometer-sized aluminum grains appeared and disappeared irregularly, and were shifted and broadened as a result of laser-induced shock wave loading. Behind the front of shock wave, large grains in aluminum foil were deformed, and subsequently exhibited grain rotation and a reduction in size. The width distribution of the diffraction spots broadened because of shock-induced grain refinement and microstrain in each grain. We performed quantitative analysis of the inhomogeneous lattice strain and grain size in the shocked polycrysalline aluminum using the Williamson-Hall method and determined the dislocation density under shock wave loading.

Microstructural deformation, and grain refinement and rotation in polycrystalline metal materials (for example, engineering alloys and ceramics) under shock compression are important characteristics, which determine material properties, such as strength and elastic-plastic deformation. Shock-induced plastic deformation and shock wave propagation in polycrystalline materials at the grain level (mesoscale) are fundamentally different from those behaviors in single-crystals and amorphous material1,2,3,4,5. Specifically, at the mesoscale, cell size-dependent features emerge, for example, particle velocity fluctuations, and rotational deformation fields. Additionally, a hierarchy of dissipative structures form, such as shear bands and heterogeneously distributed defects. Furthermore, a material is undergoing a plastic flow, the shock wave can rapidly generate dislocation slips or twinning in each grain at high strain rates (>106 s−1), whereby the dislocation density increases with strain rate, as expressed by Orowan’s law6,7,8. Laser-induced shock wave have been used for grain refinement in peening techniques, such as laser peening, for modifying surface strength, fatigue resistance, and surface feature of materials9,10,11,12,13. However, we lack a comprehensive understanding of deformation process at high strain rates. The mechanical behavior of face-centered cubic (fcc) aluminum under shock wave loading has been widely studied with the velocity interferometer system for any reflector (VISAR), which measures the displacement and thus velocity of the reflecting back surface of the sample14,15,16. To date, microstructural deformations under shock wave loading have mainly been studied in post-shock recovery experiments7,8. Molecular dynamics (MD) simulation of large-scale shock compression have been performed and the topologies of shock-compressed structure compares well with observations in transmission electron microscopy (TEM) studies of shock-induced plasticity in samples7,8,17,18. However, the dislocation density in simulations is typically greater than that in experimental observations of recovered samples. Although the grain deformation of polycrystalline materials under plastic shock flow occurs through the nucleation and movement of dislocations behind the shock wave front, plastic deformation has been primarily studied using the final shock recovery products. The post-shocked structure might have thermally recovered, and is influenced by the shock wave reflection and the residual high temperature after release of the shock pressure. Recently, the slip process of shock-compressed solid materials has been observed by Laue diffraction with broadband X-rays19,20,21,22,23,24 and an X-ray free electron laser25. In the plastic deformation of polycrystalline copper under compression at low strain rate, the initially large grains break down and rotate, which is inherent to plastic deformation26,27,28,29. The application of stroboscopic time-resolved X-ray diffraction using the intense, broadband X-ray pulses enables in situ characterization of plastic deformation in shock-compressed polycrystalline materials.

In this paper, we quantitatively analyze the shock-compressed microstructure deformation of polycrystalline aluminum using time-resolved X-ray diffraction. Because of the broad bandwidth energy (ΔE/E = 1.45%) of the X-ray pulse, we were able to observe the dynamic process of grain refinement and fragmentation in the shock-compressed materials from the X-ray diffraction patterns. Furthermore, we observed the evolution and arrangement of diffraction spots on Debye-Scherrer rings in situ. These features derive from individual crystallites and enabled us to determine the in situ dislocation density.

We performed single-shot, time-resolved, broad-bandwidth X-ray diffraction using the NW14A beamline at the Photon Factory Advanced Ring of the High Energy Accelerator Research Organization19,30,31,32. The experimental setup is shown in Fig. 1a. The sample target was composed of two layers: a polycrystalline aluminum film and a polymer film for the ablator. The aluminum used in this study was 99.9% pure aluminum foil (Nilaco, Co., Japan), which was produced by an ordinary sheet rolling; the target size was 5 × 5 × 0.05 mm3. The cover film was used for the laser ablation plasma was 25 μm-thick polyethylene terephthalate. The polycrystalline aluminum foil specimen was coated with a plastic film to produce the laser ablation plasma plume for generating the shock wave into the aluminum foil. The interval between the x-ray pulse and laser pulse at 0 ns on the sample surface was adjusted to 50% of InGaAs photodiode with 80 ps time resolution. Figure 1b shows the timing chart of the X-ray pulse (100 ps) and laser pulse (8 ns).

Time-resolved X-ray diffraction and microstructure of polycrystalline aluminum. (a) Plasma-confined sample of a polyethylene terephthalateT ablator film (25-μm thick) and polycrystalline aluminum foil (50 μm thick), and set-up of the single-shot time-resolved pink X-ray diffraction in the transmission X-ray diffraction geometry. (b) Timing chart of the synchronization system between the laser and X-ray pulses. The pulse width of the X-ray and laser are 100 ps and 8 ns, respectively. The X-ray pulse is initiated at t = 0 ns when the laser pulse reaches 50% intensity of its maximum intensity. (c) Orientation color-coded electron back-scatter diffraction map (vertical direction of the map projected in the standard triangle) of the initial microstructure of polycrystalline aluminum.

The microstructures of polycrystalline aluminum foil is shown in Fig. 1c, from which initial grain orientation and grain size can be determined. The grain size was distributed from several tens of micrometers to approximately hundred micrometers. The powder diffraction data were obtained from the samples in transmission X-ray geometry. Typical Debye-Scherrer rings from the polycrystalline aluminum foil at ambient pressure and 30 ns after laser irradiation are presented in Fig. 2. Small diffraction spots originating from individual large grains inside the polycrystalline aluminum (as shown in Fig. 1c), were present on the diffraction rings. The Debye-Scherrer ring was composed of 111, 200, 220, and 311 of aluminum. The features in the Debye-Scherrer rings in the azimuthal-angle direction become significantly smoother after shock wave propagation at 30 ns. The number of diffraction spots and broadening increased as a results of laser-shock fragmentation, which causes the formation of dislocation networks, subgrain, intergranular stress and grain fracture.

Two-dimensional diffractogram of polycrystalline aluminum. Diffraction images of polycrystalline aluminum foil before laser irradiation (left image) and at 30 ns (right image). Debye-Scherrer rings of the sample are from the 111, 200, 220, 311, and 222 reflections. After laser-induced shock wave loading, the Debye-Scherrer ring was smoothed by shock-induced plastic deformation.

During shock compression, the average shock pressure in the polycrystalline aluminum foil was estimated from the average radial diffraction peak shift, ΔG, where the lattice strain is given by \(\epsilon \) = −ΔG/G and the volumetric strain is ΔV/V = 3\(\epsilon \) under isotropic and hydrostatic conditions in a given grain. The integrated profiles in the azimuthal angle comprising the aluminum 111 and 200 reflections are shown in Fig. 3a as a function of delay time. To accurately determine the average peak shift and shape, 25 diffraction images were taken at different samples at each delay time. At t = −3 ns, the compressed bulk region begins to increase while the shock wave propagates from the aluminum surface. Because of the choice of t = 0, the laser pulse front-tail reaches the sample at this negative delay time. The physical starting time t0, at which the shock wave is generated at the sample surface, is at about −6 ns. At tmax = 3 ns, the entire probed region is maximally compressed by shock wave loading, after which the pressure begins to release because the shock wave has reached the back surface of the sample and is being reflected into a rarefaction wave. From tmax = 3 ns, we calculated the average shock pressure in the compressed region, PH, the shock wave velocity, Us, and the particle velocity, up, from the shift of the 111 peak and from the Hugoniot equation of state of aluminum. The shocked pressure from the Hugoniot relationship is given by

where \({\rho }_{0}\) denotes the initial density of aluminum, C0 is the velocity of sound in aluminum, s is the shock data parameter of aluminum, and \(\eta \) is the compressive volumetric strain. The value of \(\eta \) is found by

Estimation of shock pressure from the strain. (a) X-ray diffraction profiles of the 111 and 200 aluminum peaks at ambient pressure (black curves) and at delay times of −3, 0, 3 and 6 ns (red curves). The maximum peak shift is at 3 ns with a peak lattice strain \(\epsilon \) = −0.02. These diffraction profiles were averaged from 25 diffraction images taken from different targets. (b) Example Velocimetery interferometer systems for any reflector (VISAR) trace for the same experimental conditions as the time-resolved X-ray diffraction measurement. This velocity profile is from the free-surface of the polycrystalline aluminum film.

There is a linear relationship over the Hugoniot elastic limit between the shock wave velocity and the particle velocity such that \({U}_{s}={C}_{0}+s{u}_{p}\), where the values for C0 (5.386 km/s) and s (1.339) correspond were the same as those used in ref.33. Therefore, the average shock pressure in the entire region compressed by the shock wave was estimated to be 5.43 GPa at 3 ns. After 3 ns, the shock pressure released to ambient pressure. The estimated peak pressure of 5.43 GPa at t = 3 ns greatly exceeds the Hugoniot elastic limit of commercial pure aluminum with 50 μm thickness (about 1 GPa)34,35. Figure 3b shows the VISAR trace for the the same sample and laser energy; the free surface velocity of the polycrysalline aluminum corresponds to the rise time of the laser pulse shape. The peak pressure of pressure profile was 8.4 GPa. At 3 ns delay times, the shock wave close to the free surface, and the pressure profile can be deduced by the VISAR data, it was a 8.4 GPa peak pressure of shock wave followed by a rarefaction wave, and the average pressure was consistent with the results which estimated from the X-ray diffraction.

The diffraction peak widths of each diffraction spot represent the mosaicity of the reflecting grains during and after shock wave-induced elastic-plastic deformation. To display the spottiness in the diffraction pattern as a function of delay time, the differential aluminum 111 and 200 Debye-Scherrer rings were straightened to the azimuthal angle and are shown in Fig. 4. The diffraction images before laser irradiation were subtracted from those of the shocked samples. Each diffraction spot, which satisfied by the Bragg’s law, corresponded to an individual grain. At t = −3 ns, a few Bragg spots shifted to high Q side, whereas others did not move, corresponding, respectively to crystal volumes affected by the shock front and those in an uncompressed region.

Microstructural deformation behind the shock wave front. Differential intensity from the Debye-Scherrer ring at −3, 0, 3 and 6 ns straightened into azimuthal-angle (that is, scattering-vector) plots. (Inset) At −3 ns, a few Bragg diffraction spots from just behind the shock wave front shift to the high Q region, which corresponds to the radial direction.

The peak shifts of the diffraction spots, as shown in the magnification in Fig. 4, indicate that uniaxial shock compression of the individual grains behind the shock front took place. The elastically deformed grains were located just behind the shock wave front. This shift results from the elastic compression of one grain by an elastic precursor shock wave19. Subsequently, the plastic shock wave mainly deformed and reduced the size of each aluminum grain of on sub-nanosecond time scale after 0 ns36.

As the shock wave propagates into the aluminum sample, at t = 0 ns and 3 ns, azimuthally broadened diffraction spots evolve and the original spots begin to disappear. Broaden of the diffraction spots occurred from plastic deformation processes under shock-induced shearing and twisting, such as the induction of dislocations and dislocation networks, the formation of subgrains, grain refinement and (sub-)grain rotation. Notably, the spottiness of the rings transforms to a smooth dispersion at t = 6 ns, revealing grain refinement to less than 1 μm26,27. A plastic shock flow follows the elastic shock wave, generating many defects and dislocations inside the shock-compressed region. The appearance of new broadened diffraction spots and the disappearance of the original sharp diffraction spots, and the ultimate appearance of a continuous Debye-Scherrer ring, indicates that plastic deformation occurs inside aluminum grains in the plastic shock flow. The appearance of new diffraction spots from the fractured small grains indicated dynamic grain rotation due to grains shearing and twisting in the plastic shock flow. These small grains, which originally have reciprocal lattice vectors that lie off the Evald sphere, move into the Laue condition26 and diffract X-rays under plastic shock wave loading. Grain rotation by thermomechanical processes into the preferred orientation at conventional, slow deformation rates is inherent to plastic deformation9,26,27,37. Similarly at high strain rates, ultrasmall grains are produced when the shock wave propagates through the large mother grain, rotating them under further plastic shock flow.

Figure 5a–d show the obtained histograms of the full width at half maximum (FWHM) for the reflection spots of aluminum 200 reflection at different delay times. The distribution shifted and uniformly broadened with shock wave propagation. The number of broadened peaks increased as the shock wave propagated through the polycrystalline aluminum foil. We counted approximately 1300 individual diffraction spots on each Debye-Scherrer ring at Ghkl, which were acquired from 25 different diffraction images before and under shock compression. The diffraction spots were fitted by a Gaussian function to acquire a FWHM of ΔQ = ΔGhkl at Ghkl. The peak shift of the histogram also shifted and saturated at 3 ns because the shock wave had already arrived at the back surface, as shown in Fig. 5e. The stress rise time is related to the dislocation density and time scale on which dislocations grow with grain refinement and undergo rotation under plastic shock wave loading. For shock rise times on the order of a few nanoseconds, the width of the shock front became shorter than the aluminum grain sizes (i.e., a few ten to hundred micrometers), and complex shock wave interactions with grain boundaries arose together with inclusions, and crystal anisotropy. Such complexity might induce microstructure deformation of the polycrystalline metal.

Williamson-Hall analysis of shock compressed polycrystalline aluminum. (a–d) Width distribution of the Bragg diffraction peak of the 111 aluminum reflection along the radial direction at ambient pressure (black curve) and at delay time of −3, 0, 3 and 6 ns (red curves). All data points of the Bragg diffraction spots were obtained from the average of 25 diffraction images. The Bragg diffraction spots broaden with shock wave loading. (e) Time-evolution of the center of the peak width distribution of the 200 reflection. (f) Williamson-Hall plot of aluminum during shock compression at 6 ns. The dotted line was fitted to the shock compression data using Eq. (3).

We estimated the coherent grain size D and the inhomogeneous lattice strain \(\epsilon \) under shock wave loading from the radial-width distribution of the diffraction spots. On the basis of the Williamson-Hall (W-H) approach38 and an expression in reciprocal space39, the total line width ΔQ comprised three sample-dependent terms: the Fourier transform of the coherent crystal size along \(G\in Q\), which is equal to \(K\cdot 2\pi \)/D, where K is a shape factor equal to K = 0.94 for spherical particles; a strain-broadening term, \(|\epsilon |\) = ΔG/G; and an instrument-broadening term, Δ\({Q}_{inst}(Q)\). We define \(G=2\pi \)/d, in contrast to d* = 1/d in39, where d is a lattice spacing. Therefore, the Scherrer equation can be rewritten as:

Figure 5f shows the Williamson-Hall plot comprising the aluminum 111, 200, 220, and 311 reflections before and 6 ns after laser irradiation, at which time the first shock wave has propagated through the sample. We assumed that the instrumental-broadening term, Δ\({Q}_{inst}(Q)\), reflects the broadening of diffraction from the large aluminum crystallites before shock compression. We subtracted each distribution peak before laser irradiation from each distribution at 6 ns. These values can be determined from the slope and y-intercept of the fitting line using Eq. (3). Upon compression, there is a considerable increase of ΔQ for all reflections, which can be fitted by Δ\(Q=A+BQ\), with A = 0.18 ± 0.03 nm−1 and B = 0.0021 ± 0.00066, which gives [from Eq. (3)] values of D = 33 nm and \(\epsilon \) = 0.21 × 10−2. These result indicate that grains of polycrystalline material behind the shock wave decreased considerably from the micro- to nanometer scale. The shock recovery sample also showed grain refinement and many twins inside grain (Supplementary Fig. S1). The dislocation density (\(\rho \)) of the polycrystalline aluminum under shock wave loading, which is related to the plastic deformation, can be defined in term of the microstrain and grain size38,40,

where b is the magnitude of the Burgers vector for dislocation (0.286 nm for aluminum). Diffraction peak-broadening analysis based on the Williamson-Hall plot yields a dislocation density of 0.77 × 1015 m−2. Thus, the shock-induced deformation results in a microstructure that consists of ultrafine, nanometer-sized small grains with an increased dislocation density. The estimated dislocation density are 102 to 104 times lower than those of molecular dynamics simulations with face-centered cubic metals under shock wave loading36. However, the value of estimated dislocation density of shocked polycrystalline aluminum is consistent with the Meyers model (Supplementary Fig. S2), which was included with the dislocation moving at the shear wave velocity8. So far, in shock recovery experiments, the shock induced dislocation density observed by ex-situ experiments was low for the model. This previous result indicated that shock recovery experiments have shown that annihilation of shock induced dislocation occur during releasing the shock pressure.

Our observation demonstrated the possibility of studying the grain refinement process of materials under shock compression in situ by time-resolved synchrotron X-ray diffraction. Although laser-induced shock deformation has been applied industrially for laser peening, it remains difficult to gain in situ mechanistic insight into grain refinement and the increase in surface hardness. We directly observed grain refinement and the structural changes of polycrystalline metal under shock wave loading. Our technique will be valuable for revealing the mechanism of microstructural change of various alloy and ceramics materials based on dynamic processes.

The in situ crystalline size, microstrain, and dislocation density of polycrystalline aluminum can be determined from number of the spots in the Debye-Scherrer ring. Behind the shock wave front, large grains were compressed elastically along the shock wave direction. Ultrasmall grains of aluminum with high dislocation densities were generated under the subsequent plastic shock flow, and grains of aluminum were rotated owing to this plastic deformation. A number of ultra-fine grains were produced in the polycrystalline aluminum foil with a high dislocation density, which increased with the propagation of the laser-driven shock wave. Overall, these finding demonstrate the ability to study microstructural deformation in plastic shock flows from the atomic to mesoscale level.

Measurements were all performed in a single shot pump-probe mode using a Nd:YAG laser (Powerlite 8000 Pro; Continuum Inc., CA, USA), which was operated at a wavelength of 1064 nm with a pulse width of 8 ns to to produced a shock wave into the sample. The laser spot size on the aluminum surface was 0.5 mm in diameter. The external laser trigger from the synchrotron radio-frequency master clock was reduced from 508 MHz to 9.46 Hz using frequency dividers. A detailed description of the timing system for the laser and X-ray pulse is given in refs 19,30. Timing jitter between the laser and X-ray pulse was about 1 ns. The laser intensity was 0.8 J/pulse. The default X-ray pulse from an undulator with a period length of 20 mm were 100 ps, 109 photons/pulse, 15.61 keV, λ = 0.07949 nm, and k = 79.04 nm−1 respectively. X-ray was a 15% energy bandwidth of an asymmetric spectrum. For further monochromatization, the energy bandwidth and spectral shape were adjusted, such that the pulse possessed a symmetrical Gaussian shape of Δk/k = 1.46% using an X-ray multilayer optics41, where the focused spot size of the X-ray pulse at the aluminum surface was 450 × 250 μm2. A two-dimensional Debye-Scherrer ring was recorded for each delay-time between the laser-pump and the X-ray pulse, using a 165-mm-diameter charge-coupled device camera (MarCCD165, Rayonix Inc., IL, USA). A one-dimensional diffractogram was then created by integrating the detected Debye-Scherrer ring pattern along the azimuthal angle. A fresh area on the sample was used for each shot because the laser-irradiated area was completely destroyed after exposure of one laser shot. Finally, the laser beam direction was inclined by 15° from the X-ray path. The diffraction data was expressed against the modulus of the scattering vector Q = 2k sin(θ), where 2θ is the scattering angle, and the specific values \(G\in Q\) denote the reciprocal-lattice points: that is, the peak position, Ghkl, for a given reflection with Miller indices hkl.

The free-surface velocity of the polycrystalline aluminum film was recorded with a VISAR system on the rear side of the sample at the moment of shock release. The sample and laser irradiation conditions were same as those used for time-resolved X-ray diffraction. The VISAR system had a streak camera, which was synchronized with the shock-drive laser. The exact position of the VISAR system has adjusted with respect to the spot of shock-drive laser. Shock steadiness and shock planarity were guaranteed for the area that was irradiated by the X-ray pulse. The average pressure estimated from the VISAR system was in agreement with that estimated using the time-resolved X-ray diffraction method.

Park, H. S. et al. Grain-Size-Independent Plastic Flow at Ultrahigh Pressure and Strain rate. Phys. Rev. Lett. 114, 065502 (2015).

Article ADS Google Scholar

Horie, Y. & Case, S. Mesodynamics of shock waves in a polycrystalline metal. Shock wave 17, 135 (2007).

Article Google Scholar

Wang, S. J. et al. Microstructural figurepoints of phase transitions in shocked-loaded iron. Sci. Rep. 3, 1086 (2013).

Article CAS Google Scholar

Bourne, N. K., Millet, J. C. F., Chen, M., McGauley, J. M. & Dandekar, D. P. On the Hugoniot elastic limit in polycrystalline aluminum. J. Appl. Phys. 102, 073514 (2007).

Article ADS Google Scholar

Barber, J. L. & Kadau, K. Shock-front broadening in polycrystalline materials. Phys. Rev. B 77, 144106 (2008).

Article ADS Google Scholar

Loveridge-Smith, A. et al. Anomalous Elastic Response of Silicon to Uniaxial Shock Compression on Nanosecond Time Scales. Phys. Rev. Lett. 86, 2349 (2001).

Article ADS CAS Google Scholar

Meyers, M. A. et al. Laser-induced shock compression of monocrystalline copper: characterization and analysis. Acta Materialia 51, 12111 (2001).

Google Scholar

Cao, B. Y. et al. Effect of shock compression method on the defect substructure in monocrystalline copper. Mater. Sci. Eng. A 409, 270 (2005).

Article Google Scholar

Peyre, P., Fabbro, R., Merrien, P. & Lieurade, H. P. Laser shock processing of aluminum alloys. Application to high cycle fatigue behavio. Mat. Sci. and Eng. A 210, 196 (1996).

Article Google Scholar

Montross, C. S., Wei, T., Ye, L., Clark, G. & Mai, Y. W. Laser shock processing and its effect on microstructure and properties of metal alloys: a review. Int. J. Fatigue 24, 1021 (2002).

Article CAS Google Scholar

Hfaiedh, N. et al. Finite element analysis of laser shock peening of 2050-T8 aluminum alloy. Int. J. Fatigue 70, 480 (2015).

Article CAS Google Scholar

Ye, C., Liao, Y. & Cheng, G. J. Warm Laser Shock Peening Driven Nanostructure and Their Effect on Fatigue Performance in Aluminum Alloy 6160. Adv. Eng. Mat. 12, 291 (2010).

CAS Google Scholar

Chen, H., Yao, Y. L., Kysar, J. W., Noyan, I. C. & Wan, Y. Fourier analysis of X-ray micro-diffraction profiles to characterize laser shock peened metals. Int. J. Solid. Struct. 42, 3471 (2005).

Article Google Scholar

Huang, H. & Asay, J. R. Compressive strength measurements in aluminum for shock compression over the stress range of 4–22 GPa. J. Appl. Phys. 98, 033524 (2005).

Article ADS Google Scholar

Budzevich, M. M., Zhakhovsky, V. V., White, C. T. & Oleynik, I. I. Evolution of Shock-Induced Orientation-Dependent Metastable States in Crystalline Aluminum. Phys. Rev. Lett. 109, 125505 (2012).

Article ADS Google Scholar

Gurrutxaga-Lerma, B., Balint, D. S., Dini, D., Eakins, D. E. & Sutton, A. P. Attenuation of the Dynamic Yield Point of Shocked Aluminum Using Elastodynamics Simulations of Dislocation Dynamics. Phy. Rev. Lett. 114, 174301 (2015).

Article ADS Google Scholar

Shehadeh, M. A., Bringa, E. A., Zbib, H. M., McNaney, J. M. & Remington, B. A. Simulation of shock-induced plasticity including homogeneous and heterogeneous dislocation nucleations. Appl. Phys. Lett. 89, 171918 (2006).

Article ADS Google Scholar

Zependa-Ruitz, L. A., Strukowski, A., Oppelstrup, T. & Bulatov, V. V. Probing the limits of metal plasticity with molecular dynamics simulations. Nature 550, 492 (2017).

Article ADS Google Scholar

Ichiyanagi, K. et al. Shock-induced lattice deformation of CdS single crystal by nanosecond time-resolved Laue diffraction. Appl. Phys. Lett. 91, 231918 (2007).

Article ADS Google Scholar

Ichiyanagi, K. & Nakamura, K. G. Structural Dynamics of Materials under Shock Compression Investigated with Synchrotron Radiation. Metals 6, 17 (2016).

Article Google Scholar

Suggit, M. J. et al. Nanosecond white-light Laue diffraction measurements of dislocation microstructure in shock-compressed single-crystal copper. Nat. Commun. 3, 1224 (2012).

Article Google Scholar

Comley, A. J. et al. Strength of Shocked Load Single-Crystal Tantalum [100] Determined using In Situ Broadband X-ray Laue diffraction. Phys. Rev. Lett. 110, 115501 (2013).

Article ADS CAS Google Scholar

Wehrenberg, C. E. et al. Lattice-level observation of the elastic-plastic relaxation process with subnanosecond resolution in shock-compressed Ta using time-resolved in situ Laue diffraction. Phys. Rev. B 92, 104305 (2015).

Article ADS Google Scholar

Turneaure, S. J., Renganathan, P., Winey, J. M. & Gupta, Y. M. Twining and Dislocation Evolution during Shock Compression and Release of Single Crystals: Real-Time X-ray Diffraction. Phys. Rev. Lett. 120, 265503 (2018).

Article ADS CAS Google Scholar

Milathianaki, D. et al. Femtosecond Visualization of Lattice Dynamics in Shock-Compressed Matter. Science 342, 220 (2013).

Article ADS CAS Google Scholar

Liss, K.-D. & Yan, K. Themo-mechanical processing in a synchrotron beam. Mat. Sci. and Eng. A 528, 11 (2010).

Article Google Scholar

Yan, K. et al. From Single Grains to Texture. Adv. Eng. Mater. 11, 771 (2009).

Article CAS Google Scholar

Liss, K.-D. et al. In Situ Observation of Dynamic Recrystallization in the Bulk of Zirconium Alloy. Adv. Eng. Mater. 11, 687 (2009).

Google Scholar

Liss, K.-D. et al. In situ study of dynamic recrystallization and hot deformation behavior odd a multiphase titanium aluminide alloy. J. Appl. Phys. 106, 11352 (2009).

Google Scholar

Nozawa, S. et al. Developing 100 ps-reoslved X-ray structural analysis capabilities on beamline NW14A at the Photon Factory Advanced Ring. J. Synch. Rad. 14, 313 (2007).

Article CAS Google Scholar

Hu, J. et al. Complex structural dynamics of bismuth under laser-driven compression. Appl. Phys. Lett. 103, 161904 (2013).

Article ADS Google Scholar

Ichiyanagi, K. et al. Shock-induced intermediate-range structural change of SiO2 glass in the nonlinear elastic region. Appl. Phys. Lett. 101, 181901 (2012).

Article ADS Google Scholar

Michell, A. C. & Nelis, W. J. Shock compression of aluminum, copper, and tantalum. J. Appl. Phys. 52, 3363 (1980).

Article ADS Google Scholar

Kanel, G. I. Uniaxial behavior of usual materials in shock waves. J. Phys: Conference Series 500, 012001 (2014).

ADS Google Scholar

Zaretsky, E. B. & Kanel, G. I. Effect of temperature, strain, and strain rate on the flow stress of aluminum under shock-wave compression. J. Appl. Phys. 112, 073504 (2012).

Article ADS Google Scholar

Bringa, E. M. et al. Shock deformation of face-centered-cubic metals on subnanosecond timescales. Nat. Mater. 5, 805 (2006).

Article ADS CAS Google Scholar

Margulies, L., Winther, G. & Poulsen, H. F. In Situ Measurement of Grain Rotation during Deformation of Polycrystals. Science 291, 2892 (2001).

Article Google Scholar

Williamson, G. K. & Smallman, R. E. III. Dislocation densities in some annealed and cold-worked metals from measurements on the X-ray debye-scherrer spectrum. Phil. Mag. 1, 34 (1956).

Article ADS CAS Google Scholar

Mittemeijer, E. J. & Welzel, U. The state of the art of the diffraction analysis of crystallite size and lattice strain. Z. Fur. Krist. Int. J. Struct. Phys. Chem. Asp. Cryst. Mater. 223, 552 (2009).

Google Scholar

Smallman, R. E. & Westmacott, K. H. Stacking fault in face-center cubic metals and alloy. Phil. Mag. 2, 669 (1957).

Article ADS CAS Google Scholar

Ichiyanagi, K. et al. 100 ps time-resolved solution scattering utilizing a wide-bandwidth X-ray beam from multilayer optics. J. Synchrotron. Rad. 16, 391 (2009).

Article CAS Google Scholar

Download references

Financial support was provided by the Amada Foundation for Laser Processing and the Toray Science Foundation. This work supported by a JSPS Grant-in-Aid for Young Scientists (A) (grant number 17H04820), JSPS Grant-in-Aid for Challenging Exploratory Research (grant number 17K18999), and Grant-in-Aid for Scientific Research on Innovation Areas “Soft Crystals” (Area 2903, grant number 17H06372). This work was performed with the approval of the Photon Factory Advisory Committee (proposal numbers 2013G624 and 2015S2-006). We thank Adam Brotchie, PhD, from Edanz Group (www.edanzediting.com/ac) for editing a draft of this manuscript. The time-resolved X-ray diffraction systems have been developed by a JSPS Grant-in-Aid for Young Scientists (A) (grant number 17H04820), the Toray science foundation and an Amada foundation for Laser processing. The Velocity Interferometer Systems for Any Reflector had been developed by a JSPS Grant-in-Aid for Challenging Exploratory Research (grant number 17K18999), and Grant-in-Aid for Scientific Research on Innovation Areas “Soft Crystals” (Area 2903, grant number 17H06372).

Division of Biophysics, Department of Physiology, Jichi Medical University, 3311-1 Yakushiji, Shimotsuke, Tochigi, 329-0498, Japan

Kouhei Ichiyanagi

Photon Factory, Institute of Materials Structure Science, High Energy Accelerator Research Organization, 1-1 Oho, Tsukuba, Ibaraki, 305-0801, Japan

Kouhei Ichiyanagi, Sota Takagi, Ryo Fukaya, Shunsuke Nozawa, Masao Kimura & Shin-ichi Adachi

Division of Earth Evolution Science, Graduate School of Life and Environmental Sciences, University of Tsukuba, 1-1-1 Tennodai, Tsukuba, Ibaraki, 305-8572, Japan

Sota Takagi

Institute of Pulsed Power Science, Kumamoto University, 2-39-1 Kurokami, Kumamoto, 860-8555, Japan

Nobuaki Kawai

Laboratory for Materials and Structures, Institute of Innovative Research, Tokyo Institute of Technology, R3-10, 4259 Nagatsuta, Yokohama, Kanagawa, 226-8503, Japan

Kazutaka G. Nakamura

Materials Science and Engineering Program, Guangdong Technion- Israel Institute of Technology, 241 Daxue Road, Jinping District, Shantou, Guangdong, 515063, China

Klaus-Dieter Liss

Technion - Israel Institute of Technology, Haifa, 32000, Israel

Klaus-Dieter Liss

You can also search for this author in PubMed Google Scholar

K.I., N.K., S.T., R.F. and S.N., performed time-resolved X-ray diffraction experiments. M.K. performed microscopy. K.I. analyzed the results of X-ray diffraction data. K.I., S.T. and S.N. prepared the laser and timing systems at the NW14A beamline. S.N. and S.A. arranged the beam-time. K.L. and K.N. provided useful discussion. K.I. reviewed the manuscript.

Correspondence to Kouhei Ichiyanagi.

The authors declare no competing interests.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and permissions

Ichiyanagi, K., Takagi, S., Kawai, N. et al. Microstructural deformation process of shock-compressed polycrystalline aluminum. Sci Rep 9, 7604 (2019). https://doi.org/10.1038/s41598-019-43876-2

Download citation

Received: 23 June 2017

Accepted: 27 April 2019

Published: 20 May 2019

DOI: https://doi.org/10.1038/s41598-019-43876-2

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Materials Science: Materials in Electronics (2021)

Shape Memory and Superelasticity (2021)

Journal of Materials Science: Materials in Electronics (2021)

Journal of Materials Science: Materials in Electronics (2020)

Journal of Nanostructure in Chemistry (2020)

Microstructural deformation process of shock-compressed polycrystalline aluminum | Scientific Reports